GAS WELDING & BRAZING

34

Gas Welding

& Brazing

Welding Positions

Standards

Mechanical Properties

Cu Si

60.0

Sn

0.30

Zn

34.0

0.30

EN 1044 : Cu 302

BS 1845 CZ 6A 1453 C2

Melting Point ºC 875

UTS N/mm2 420

Hardness BHN 120

• A flux impregnated silicon bronze rod which is perfect for

brazing clean mild steel components and is ideally suited for

use in motor body shops and sheet metal fabrications

• Automotive, sheet metal and tubular furniture manufacturers

Product Information

Current Type

Recommended Gas

Oxygen/Acetylene

Approvals on request

Manufacturer's Approvals

Chemical Composition

2.5kg Tube (500mm length)

BRONZE C2 K (FLUX IMPREGNATED)

Welding Positions

Standards

Mechanical Properties

Si

0.30

Sn

0.30

Zn

34.0

Cu

60.0

EN 1044 : Cu302

BS 1845 CZ6A 1453 C2

Melting Point ºC 875

UTS N/mm2 420

Hardness BHN 120

Features and Applications

• Flux coated silicon bronze rod for continuous brazing through

not having to flux dip the rod. Ideal for general mild steel,

galvanised steel, dissimilar joints and DIY enthusiasts

• Automotive, tubular furniture, repair and maintenance DIY

Product Information

Current Type

Recommended Gas

Oxygen/Acetylene

Chemical Composition

2.5kg Tube

Approvals on request

Manufacturer's Approvals

FLUX COATED BRONZE C2FC

Pt No. Diameter

7473 2.4mm

7474 3.2mm

Pt No. Diameter

7476 2.4mm

7477 3.2mm

Features and Applications

Index

  1. Page 0001
  2. Page 0002
  3. Page 0003
  4. Page 0004
  5. Page 0005
  6. Page 0006
  7. Page 0007
  8. Page 0008
  9. Page 0009
  10. Page 0010
  11. Page 0011
  12. Page 0012
  13. Page 0013
  14. Page 0014
  15. Page 0015
  16. Page 0016
  17. Page 0017
  18. Page 0018
  19. Page 0019
  20. Page 0020
  21. Page 0021
  22. Page 0022
  23. Page 0023
  24. Page 0024
  25. Page 0025
  26. Page 0026
  27. Page 0027
  28. Page 0028
  29. Page 0029
  30. Page 0030
  31. Page 0031
  32. Page 0032
  33. Page 0033
  34. Page 0034
  35. Page 0035
  36. Page 0036
  37. Page 0037
  38. Page 0038
  39. Page 0039
  40. Page 0040
  41. Page 0041
  42. Page 0042